凝固条件对AlSi7Mg合金半固态加热时组织的影响

毛卫民, 钟雪友

毛卫民, 钟雪友. 凝固条件对AlSi7Mg合金半固态加热时组织的影响[J]. 工程科学学报, 1998, 20(3): 253-257. DOI: 10.13374/j.issn1001-053x.1998.03.032
引用本文: 毛卫民, 钟雪友. 凝固条件对AlSi7Mg合金半固态加热时组织的影响[J]. 工程科学学报, 1998, 20(3): 253-257. DOI: 10.13374/j.issn1001-053x.1998.03.032
Mao Weimin, Zhong Xueyou. Effect of the Solidification Conditions on the Microstructures of AlSi7Mg Alloy during Semi-solid Remelting[J]. Chinese Journal of Engineering, 1998, 20(3): 253-257. DOI: 10.13374/j.issn1001-053x.1998.03.032
Citation: Mao Weimin, Zhong Xueyou. Effect of the Solidification Conditions on the Microstructures of AlSi7Mg Alloy during Semi-solid Remelting[J]. Chinese Journal of Engineering, 1998, 20(3): 253-257. DOI: 10.13374/j.issn1001-053x.1998.03.032

凝固条件对AlSi7Mg合金半固态加热时组织的影响

基金项目: 

国家“863”基金资助项目

详细信息
    作者简介:

    毛卫民,男,39岁,副教授

  • 分类号: TG292

Effect of the Solidification Conditions on the Microstructures of AlSi7Mg Alloy during Semi-solid Remelting

  • 摘要: 利用电阻炉研究了凝固条件对AlSi7Mg 合金半固态加热时组织的影响.研究表明:电磁搅拌的AlSi7Mg 合金在589或597℃下保温,在较短的时间内(5~10 min),共晶体即可重熔,α相可转变为球状,而且保温温度越高,试样共晶体重熔和α相球化的过程越快;相比较,未电磁搅拌的细小枝晶的AlSi7Mg 合金在同样的加热温度下,即使保温60min,也无法获得完全球状α相的半固态组织.
    Abstract: The effect of the solidification conditions on the microstructures was studied during partial remelting of AlSi7Mg alloy with the help of an electrical pipe-type furnace. The results show that the eutectic is remelted above all and α phases are gradually evolved into spheroidal shape, if the AlSi7Mg alloys stirred strongly by rotating electro-magnetic field during the first solidification are heated again to 589℃ or 597℃ and have been held for a short time(for example, 5~10 min), and moreover, the higher the holding temperature, the faster the eutectic remelting process and α phase's evolution are. In contrast, even though the AlSi_7 Mg alloy's samples non-stirred with fine dendritic microstructures ate heated to the same temperatures as those stirred by rotating electromagnetic field and have been held for 60 min, it is not possible to change all the dendritic α phases to speroidal α phase.
计量
  • 文章访问数:  329
  • HTML全文浏览量:  94
  • PDF下载量:  13
  • 被引次数: 0
出版历程
  • 收稿日期:  1997-10-14
  • 网络出版日期:  2021-08-26
  • 刊出日期:  1998-03-24

目录

    /

    返回文章
    返回